ASTM A335/335M Seamless Ferritic Alloy-Steel Pipe
This specification covers seamless ferritic alloy-steel pipe for high-temperature service. The pipe shall be suitable for bending,
and similar forming operations,
and for fusion welding. Grade P2 and P12 steel pipes shall be made by coarse-grain melting practice. The steel material shall conform to chemical composition,
and hardness requirements. Each length of pipe shall be subjected to the hydrostatic test. Also,
each pipe shall be examined by a non-destructive examination method in accordance to the required practices. The range of pipe sizes that may be examined by each method shall be subjected to the limitations in the scope of the respective practices. The different mechanical test requirements for pipes,
transverse or longitudinal tension test,
and hardness or bend test are presented.
This abstract is a brief summary of the referenced standard. It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application. ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate,
complete or up to date.
Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service.
Standards: ASTM A335/335M (ASME SA335/SA335M)
Outer Dimensions: 19.05mm - 114.3mm
Wall Thickness:2.0mm - 14 mm
Length: max 16000mm
Application: Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service.
The main products of steel / steel grade: P11; P12; P22; P5;.
Packing: Bare packing/bundle packing/crate packing/wooden protection at the both sides of tubes and suitably protected for sea-worthly delivery or as requested.
Inspection and Test: Chemical Composition Inspection,
Mechanical Properties Test(Tensile Strength,
Yield Strength, Elongation, Flaring,
Flattening, Bending, Hardness,
Surface and Dimension Test,
No-destructive Test, Hydrostatic Test.
Surface treatment: Oil-dip, Varnish,
Passivation, Phosphating, Shot Blasting.